Compressive Behavior of Concrete Containing Glass Fibers and Confined with Glass FRP Composites

In the last decade, the utility of fiber-reinforced polymers (FRP), which include carbon glass FRP, carbon FRP and aramid FRP, has more advantages for rehabilitation and strengthening of current structures owing to the various benefits, excessive strength and durability, portability, the ability of fixing, quick implementation, etc. GFRPs are the most prevalent types of FRPs owing to their high strength-to-price ratio Christian and Billington (2011), Bazli et al. (2016), Feng et al. (2014), Li et al. (2016), Lam et al. (2003), Tahsiri et al. (2015).

The concrete is one among the foremost vital engineering materials within the construction field. Whereas concrete has several advantages, such as high strength, sturdy deformation resistance, and low price, it additionally presents disadvantages, such as brittleness, poor malleability and poor crack resistance ( Kizilkanat et al. (2015), Shaikh et al. (2013), Meda et al. (2016), Cromwell et al. (2011)). Students and engineers have planned the incorporation of fibers to enhance the performance of concrete. Fiber-reinforced concrete offers superior tensile strength, bending resistance, shock strength, elongation, and ductility when compared to conventional concrete. It also possesses anti-shrinkage, anti-cracking, anti-freezing, and anti-corrosion characteristics.

When the cracks are developing in fiber-reinforced concrete, the fibers bear the traction forces acting on the cracks to strengthen the concrete matrices and continue to support the traction load which stops further crack development. In the literature different types of fibers have been reported, such as steel fibers, polypropylene fibers, carbon fibers, glass fibers, basalt fibers, polyvinyl alcohol fibers, and mixed fibers (Chao et al., 2009; Xie et al., 2019; Zhu et al., 2019; Feng et al., 2019; Sun et al., 2019; Signorini et al., 2020; Liu et al., 2020; Mohammad Hosseini et al. 2020). The addition of 0.5% to 1.5% steel fibers by fiber volume was found to augment the traction strength of concrete by 37–177% (Wang et al., 2019).

The fiber volume increased and it was observed that the tensile and compressive strengths first increased and then decreased In addition, fibers 6 mm long were found to be better than fibers 12 mm long. Therefore, differing kinds and lengths of fibers have different effects. Furthermore, small flexible fibers have been observed to be better suitable for controlling the formation of micro-cracks while large and stiff fibers have been proven to be more suitable for controlling the development of cracks (Ganesan et al., 2014).

Therefore, the use of a combination of different fibers can lead to certain synergistic effects. For example, the combined use of polyvinyl alcohol fibers and steel fibers help to achieve optimal tensile behavior (Liu et al., 2020). It was also shown that adding a sufficient amount of basalt fibers reduced the porosity of the concrete and thus improved its durability (Guo et al., 2019; Niu et al., 2020).

However, compressive resistance does not always increase with the percentage of GFRP in concrete, implying that there is an ideal content of GFRP in concrete in order to obtain maximum compressive strength (Di Zheng et al., 2020). For the experiments, a series of concrete specimens with varying percentages of fiber 0 wt.%, 0.4 wt.%, 0.8 wt.%, or 1.2 wt.% were employed. The experimental data reveal that the uniaxial compressive strength of fiber concrete (FRC) initially increased with 0.8 wt.% and subsequently decreased with increasing fiber dose. The optimum glass fiber content is determined by the fiber type. In principle, shorter gfs with higher length–diameter ratios are more successful at regulating the formation of tiny cracks, whereas longer gfs with lower length–diameter ratios are more effective at controlling the development of micro-cracks (Kasagani and Rao 2018) .

In contrast, the lateral limiting stress furnished with the aid of using wrapped FRP jacket will increase constantly with lateral evolution because of the linear elastic conduct of FRP. As a result, this sort of lateral inclusion modifies the compression conduct of regular concrete and results in compression hardening conduct (Mirmiran & Shahawy, 1997; Spoelstra & Monti, 1999). It is hypothesized that the inclusion-induced compressive strain of FRP are also applicable to glass fiber-containing concrete.

The combination of glass fiber-containing concrete (GFCC) wrapped with an FRP jacket can improve the overall performance of concrete. Thus, the unique combined properties in compression and tension of FRP-confined GFCC have great potential to optimize and improve the performance of structural components. It is necessary to prove this hypothesis experimentally and to observe the interactions among FRP and GFCC in such configurations.

The originality of this study consists in the evaluation of the effect of wrapped FRP jacket of concrete containing different percentages of glass fibers on strength properties and failure mechanism of fiber-reinforced concrete, and the axial strength versus strain responses of GFCC cylinders externally confined with GFRPs. Another goal of this study is to evaluate the applicability of the strength force models (which are mainly developed for special FRPs) at GFR–GFCC. For this purpose, 48 GFCC cylinders were created and tested under monotonous axial compression. The research parameters included the concrete strength (such as 25 MPa, 16 MPa and 8.5 MPA), the fiber percentages (0 wt.%, 0.3 wt.%, 0.6 wt.%, 0.9 wt.%, 1.2 wt.%) and the layers of the GFRP (2 layers, 4 layers, 6 layers).

In order to evaluate the feasibility of this new composite material, the behavior of glass fiber-containing concrete (GFCC), which is by glass fiber-reinforced polymer (GFRP) composites, was investigated under axial compression. For this aim, 48 round concrete columns were built and examined; the diameter and height of the concrete columns were 150 mm and 300 mm, respectively, Fig. 1. The test programmer is summarized in Table 1. It is divided into four groups according to the type of concrete strength, the number of layers of glass-GRP composite materials and the proportion of reinforcing fibers contained in the concrete.

Type I general purpose Portland cement was used as the binder in this research. Physical and chemical properties of this binder are provided in Table 2.

Alkali-resistant chopped strands of high tensile-strength GFRP were used as the fiber reinforcement; the overview and properties of GFRP are shown in Table 3. Four groups of mixed concrete were produced containing alkali-resistant fiber strengthened with percentages 0 wt.%, 0.3 wt.%, 0.6 wt.%, 0.9 wt.%, 1.2 wt.%, respectively, as by volume replacement of natural coarse aggregate; see Table 3.

Locally available bi-directional fiber glass (Fig. 2) and polyester resin were used to develop a low-cost glass fiber-reinforced polymer (GFRP) composite. This type of bi-directional fiber glass is widely used in the boating industry. The behavior of the GFRP composites was determined. Using the standard tensile coupon test, tensile coupons were made using various layers of fiber glass, such as one, two, three, four, and five layers to obtain accurate results. In addition, three tensile specimens were tested for each thickness to get average results.

The tensile specimens were tested using the UTS-SHIMADZU universal testing machine according to the standard guidelines of the ASTM D638 (1990), see Table 4.

Specimens are placed in the grips of a Universal Test Machine at a specified grip separation and pulled until failure. For ASTM D638 the test speed can be determined by the material specification or time to failure (1–10 min). A typical test speed for standard test specimens is 2 mm/min (0.05 in/min).

First gravel, sand, water and cement were weighed on an electronic scale. The fiber is light in weight and easily floats on the liquid surface. The cement, sand, gravel and fiber were added with a suitable amount of water until the fibers were sufficiently dispersed, and the prepared suspension was poured into prepared molds for tap molding.

Second, the GFRP composites were applied after 28 days. The concrete surface was properly cleaned to remove dust prior to the application of the GFRP compound. In the first step, the polyester resin was applied to the concrete surface with a brush and then a resin-soaked fiber glass board was wrapped around the circular concrete cylinder. The typical process of GFRP strengthening is shown in Fig. 3a, b and the final strengthened specimen is displayed in Fig. 3c.

Detailed instrumentation for accurate recording and control of the lateral dilation and axial strain of the GFRP-confined GFCC cylinders was used. Compressive strength tests were carried out to evaluate the strength properties of GFRP-confined GFCC cylinders using a testing machine with a capacity of 2000 KN. A total of the three LVDTs were mounted in a steel frame which was specially developed for the concrete cylinders with threaded bolts. In addition, strain gauges were installed horizontally in the GFRP mixture at mid-height of the concrete cylinders in order to record the lateral expansion and tension of FRP (Fig. 4). The specimens were loaded under compressing at a constant stroke rate of 0.1 kN/s.

Various models have been proposed in literature studies to theoretically represent the ultimate strength and strain [35–37]. Table 6 contains a list of selected models for different types of FRP compounds with different inclusion coefficients. The comparison between the estimated and experimental values is shown in Figs. 12, 13.

Fig. 12 shows the comparison between the theoretical models and experimental results of ultimate strength. It can be seen that the prediction accuracy on the ultimate strengths of concrete between the results of theoretical models and experiments are affected by the strengths of concrete. For example for concrete strength equal to 25 MPa, all models are very close to the experimental results of GFRP-confined GFCC groups. But for concrete strength equal to 16 MPa the predicted accuracies are an average estimate, and for concrete strength equal to 8.5 MPa are an overestimate.

The results indicate that the augmentation in the difference between the design strength and the experimental strength are due to the increase in in concrete strength. For concrete strength equal to 25 MPa the diffrenec are slightly higher of 8% ,5%,3% and 2% for models Ghernouti et al. (2011), Bensaid et al. (2010), AL-Salloum et al. (2007) and Teng et al. (2007) respectively. And for concrete strength equal to 16 MPa, The results indicate an increase in 13% ,18%,20% and 20% for models Ghernouti et al. (2011), Bensaid et al. (2010), AL-Salloum et al. (2007) and Teng et al. (2007) respectively. For concrete strength equal to 8.5 MPa,  The results indicate an increase in 54% ,60%,65% and 70% for models Ghernouti et al. (2011), Bensaid et al. (2010), AL-Salloum et al. (2007) and Teng et al. (2007) respectively. Although the theoretical predictions of the current models are close to the experimental results of high-strength concrete, there is still a need to develop more accurate strength models for low strength of GFRP-confined GFCC.

Fig. 13 shows the comparison between the theoretical models and experimental results of ultimate strain. The estimated values of ultimate strain models proposed by Teng et al. (2007) are quite close to the experimental results of strength of GFRP-confined GFCC equal to 25 MPa and 16 MPa. However, the theoretical predictions of Ghernouti et al. (2011), Bensaid et al. (2010) and AL-Salloum et al. (2007) are not accurate for predicting the ultimate strain, so there is still a need to develop more accurate strain models for low strength of GFRP-confined GFCC.

This paper investigates the confinement effects of glass fiber–reinforced polymer composites on circular concrete columns made with concrete contained GF. Three types of strength of concrete locally available (8.5 Mpa, 16 Mpa and 25 Mpa) were confined with GFRP. In this study, a total number of 48 circular concrete columns were constructed and tested under monotonic axial compression. Based on experimental and analytical investigations, a few conclusions are summarized below: